Ukuzinza koMqulu oLungileyo kunye noKuxhathisa ukothuka kweThermal, ukucoceka okuPhezulu kunye neRefractoriness Tabular Alumina

tabular alumina ta
izixhobo zetabular alumina
i-alumina tabular

Ingcaciso emfutshane

I-Tabular Alumina yimathiriyeli ecocekileyo efakwe kumaqondo obushushu aphezulu ngaphandle kwe-MgO kunye ne-B2O3 izongezo, i-microstructure yayo yi-polycrystalline ene-dimensional structure ene-tabular enkulu ekhuliswe kakuhle α - Al2O3 crystals.I-Tabular Alumina ine-pores encinci evaliweyo kwi-crystal ye-individval, umxholo we-Al2O3 ungaphezulu kwe-99% .Ngoko ke inozinzo oluhle lwevolumu kunye nokumelana nokutshatyalaliswa kwe-thermal, ukucoceka okuphezulu kunye nokuchasana, amandla agqwesileyo omatshini, ukuxhathisa i-abrasion ngokumelene ne-slag kunye nezinye izinto.

QHAGAMSHELANA NGOKU

Ukuqulunqwa kwemichiza

Into		i-aggregate		izohlwayo
		Isalathiso	Isiqhelo	Isalathiso	Isiqhelo
Ukwakhiwa kweekhemikhali	Al2O3 (%)	≥99.20	99.5	≥99.00	99.5
	SiO2 (%)	≤0.10	0.06	≤0.18	0.08
	Fe2O3 (%)	≤0.10	0.07	≤0.15	0.09
	Na2O (%)	≤0.40	0.28	≤0.40	0.30

Iipropati Zomzimba

Into		Isalathiso	Isiqhelo
Iipropati Zomzimba	Ubuninzi bobuninzi / cm3	≥3.50	3.58
	Ukufunxa izinga lamanzi	≤1.0%	0.75
	Izinga le-Porosity	≤4.0%	2.6

Ukuthelekisa ipropati

Into		I-Alumina yeTabular	IAlumina eFused emhlophe
Ukuthelekiswa kwepropati ye-Tabular Alumina kunye ne-White Fused Alumina	Ukubunjwa kweekhemikhali ze-homogeneity	ukulingana	I-Fine iphezulu kwi-Na2O
	I-avareji yobungakanani bepore/μm	0.75	44
	Izinga lePorosity/%	3-4	5-6
	Ubuninzi bobuninzi / cm3	3.5-3.6	3.4-3.6
	Ukuziphatha kwe-Creep/%	0.88	0.04, uvavanyo oluphezulu
	Umsebenzi wokucula	Phezulu	phantsi
	Amandla, ukuxhathisa ukothuka kwe-thermal	Phezulu	phantsi
	Ireyithi yokunxiba /cm3	4.4	8.7

Itheyibhile kunye nezinye iiAggregates

Ii-aggregates zingumqolo we-refractory formulation kwaye zibonelela ngozinzo lwe-dimensional kwimveliso ephikisayo.Amaqhezu anqabileyo ongeza ukothuka kwe-thermal kunye nokuxhathisa ukubola kwaye izohlwayo ezihlangeneyo ziphucula ukusabalalisa ubungakanani bamasuntswana kunye nokwandisa ukuchaswa kwemveliso.

Umgangatho ohambelanayo we-alumina ye-Tabular yisiphumo senkqubo ye-sinter elawulwa kakuhle kunye namaqondo okushisa omlilo ngaphezu kwe-1800 ° C. Ukusetyenziswa kwezithando zokushisa eziphakamileyo ezinobuchwephesha bezobugcisa zivumela ukuxinaniswa kwezinto ezikhethiweyo ezikhethiweyo ngaphandle kwezixhobo zokuncedisa. impembelelo embi kwiipropati zokushisa eziphezulu ze-refractories.

Njengomphumo wenkqubo ye-sinter, i-aggregates ibonisa ukubunjwa okufanayo kwe-mineralogical kunye neekhemikhali kuwo onke amaqhezu.Ngokuchasene neemveliso ezidityanisiweyo apho ukungcola kuqokelelwa kwisohlwayo, ukusetyenziswa kwe-sintered aggregates kwi-refractory formulation iqinisekisa ukuziphatha okuzinzileyo nokuthembekileyo.

IJunsheng ibonelela ngeesayithi ezahlukeneyo zeeaggregates ukusuka kumaqhezu arhabaxa kakhulu ukuya kubungakanani bomhlaba ocolekileyo <45 μm kunye <20 μm.Ukutyumza kunye nokusila kulandelwa ngamanyathelo oku-de-ironing anzulu akhokelela kwi-iron ephantsi kakhulu phakathi kwamaqhezu ahlukeneyo.

Inkqubo yeMveliso yeTabular alumina

Ukusetyenziswa kweTabular Alumina

I-Tabular Alumina yimathiriyeli ekhethwayo kwii-refractories eziphezulu ezingasebenziyo ezisetyenziswa kumashishini ahlukeneyo aquka intsimbi, isiseko, i-samente, iglasi, i-protrochemical, i-ceramic, kunye nokutshisa inkunkuma.Ezinye izicelo eziqhelekileyo ezingezizo ezinqandayo ziquka ukusetyenziswa kwayo kwifenitshala ye-kiln kunye nokucoca isinyithi.