I-Calcium Aluminate Cement, High Aluminate Cement A600, A700.G9, CA-70, CA-80

Ingcaciso emfutshane

I-porosity esezantsi, uzinzo oluphezulu lweekhemikhali, ukusebenza kobushushu obuphezulu, ukumelana nokunxiba okuphezulu

QHAGAMSHELANA NGOKU

Iimbonakalo

I-porosity esezantsi, uzinzo oluphezulu lweekhemikhali, ukusebenza kobushushu obuphezulu, ukumelana nokunxiba okuphezulu

Iinkcukacha zolwazi

Imveliso idla ngokusetyenziswa njengezixhobo ezahlukeneyo zokutshisa isinyithi, i-petrochemical, i-petroleum, oomatshini, izixhobo zokwakha kunye namanye amashishini.

I-Alumina ephezulu yeSamente CA-50

Izinto			Iyunithi	A600	A700	G9
Ukwakhiwa kweekhemikhali	Al₂O₃		%	50-60	50-60	53.5 ubuninzi
	CaO		%	33min	33.00min	33.00min
	SiO₂		%	8.00ubuninzi	8.00ubuninzi	5.50ubuninzi
	Fe₂O₃		%	2.50ubuninzi	2.50ubuninzi	2.50ubuninzi
	RO₂		%	0.4 ubuninzi	0.40ubuninzi	0.40ubuninzi
Umphezulu othe ngqo we-Aea			cm³/g	3000max	3000max	350min
Iseti yokuQala			imiz	60min	60min	90min
Ukuphelisa iSeti			h	6 ubuninzi	6 ubuninzi	6min
Ukugoba Amandla		usuku olu-1	Mpa	5.50ubuninzi	7.00min	8.00min
Ukugoba Amandla		iintsuku ezi-3	Mpa	6.50ubuninzi	8.00min	10.00min
Amandla acinezelayo		usuku olu-1	Mpa	40.00ubuninzi	50.00min	72.00min
Amandla acinezelayo		iintsuku ezi-3	Mpa	50.00 max	60.00min	82.00min
IiRefractories			℃	1350	1350	1450

I-Calcium Alumina Cement

Izinto			Iyunithi	CA-70	CA-80
Ukwakhiwa kweekhemikhali	Al₂O₃		%	68.50-72.00	78.50-81.00
	CaO		%	28.0-31.50	17.00-20.00
	SiO₂		%	≤0.50	≤0.40
	Fe₂O₃		%	≤0.50	≤0.30
	K₂O+Na₂O		%	≤0.50
Umphezulu othe ngqo we-Aea			Cm²/g	≥5000	≥7000
Iseti yokuQala			imiz	≥45	≥30
Ukuphelisa iSeti			h	≤6	≤6
Ukugoba Amandla		24h	Mpa	≥7.0	≥5.50
Ukucinezela Amandla		24h	Mpa	≥45	≥40
IiRefractories			℃	≥1600	≥1790